HALLSTAR DIOPLEX VLV is a highly efficient, very easy processing, very low viscosity polymeric plasticizer. HALLSTAR DIOPLEX VLV是一種高效的，非常容易處理，非常低粘度聚合物增塑劑。It has similar handleability profile to standard monomerics yet provides an improvement in the level of resistance to extraction by various media when compared to monomerics such as DOP, DINP and linear phthalates.它標準monomerics有類似的可操作性輪廓時，還提供了一個提高水平耐提取各種媒體如DOP，DINP和線性鄰二甲酸酯相比monomerics。
In addition, HALLSTAR DIOPLEX VLV offers excellent cold flex properties and compares favorably with most phthalates and trimellitates.此外，HALLSTAR DIOPLEX VLV提供了優良的冷彎曲性能和媲美大多數鄰二甲酸酯和偏三酸酯。
With a benign environmental / legislative profile, low viscosity is an essential ingredient in plastisol formulations as a non-phthalate.與一個良性環境/立法輪廓，中，低粘度是一個重要的成分作為非鄰二甲酸塑配方。
HALLSTAR DIOPLEX VLV IS AVAILABLE GLOBALLY. HALLSTAR DIOPLEX VLV是范圍內提供。
|
|
Suggested Uses:使用建議：
Automotive sealant, Automotive sealant, Coated fabrics, Coated fabrics, Film and sheeting for use in low temperatures, Film and sheeting for use in low temperatures, Gaskets, Gaskets, General-purpose film, General-purpose film, Low viscosity plastisols, Low viscosity plastisols, Phthalate alternative, Phthalate alternative, Pigment dispersant, Pigment dispersant, Plastisol coatings, Plastisol coatings, PVC Film, and PVC Film汽車密封膠，汽車密封膠，涂層織物，涂層織物，薄膜和塑料布，用于在氣溫低，墊片，墊圈，通用膜，通用膜，低粘度塑料溶膠，低粘度，用于在氣溫低，薄膜和薄片塑料溶膠，鄰二甲酸酯替代鄰二甲酸酯替代，顏料分散劑，顏料分散劑，增塑溶膠涂料，塑料溶膠涂層，PVC薄膜，PVC薄膜
Compatibility:兼容性：
-
Polymethyl methacrylate聚甲基丙烯酸甲酯
-
Polymethyl methacrylate聚甲基丙烯酸甲酯
-
Vinyl chloride acetate氯乙烯醋酸
-
Vinyl chloride acetate氯乙烯醋酸
Typical Properties:典型屬性：
|
Viscosity at 25°C, cSt粘度在25℃，CST
|
<100 <100
|
|
Specific Gravity, 20°C比重20℃
|
1.0 1.0
|
|
Hydroxyl Value, mg KOH/g羥值，毫克KOH /克
|
40 40
|
|
Acid Value, mg KOH / g酸值，毫克KOH /克
|
2.5 2.5
|
|
Appearance外形
|
Straw-colored稻草色
|
|
Color Hazen (PT/Cobalt)彩色哈森（PT /鈷）
性能特性：
|
In PVC-EU歐盟在PVC-
|
|
Modulus, MN/m2 100％模量，MN/m2
|
5.0 5.0
|
|
Tensile Strength, MN/m2拉伸強度，MN/m2
|
14.3 14.3
|
|
Elongation at Break, %斷裂伸長率，％
|
495 495
|
|
Shore A Hardness邵爾A硬度
|
63 63
|
|
Tg, °C TG°C
|
-32 -32
|
|
Low Temperature Brittle Point, °C低溫脆化點℃
|
-44 -44
|
|
Low Temp Gehman T10,000 PSI, °C低溫格曼T10，000 PSI，°C
|
-36 -36
|
|
Volatilization揮發
|
-13.3 -13.3
|
|
Immersion/Extraction, Weight change, %浸入/提取，重量變化，％
|
|
|
Mineral Oil礦物油
|
-16.6 -16.6
|
|
Olive Oil橄欖油
|
-17.1 -17.1
|
|
Hexane正己烷
|
-22.7 -22.7
|
|
Distilled water蒸餾水
|
-1.1 -1.1
|
|
1% Soap Solution 1％的肥皂溶液
|
-9.2 -9.2
|
|
|
In PVC-US在PVC美
|
|
Shore A Hardness邵爾A硬度
|
63 63
|
|
Elongation at Break, %斷裂伸長率，％
|
495 495
|
|
Tensile Strength, MPa拉伸強度，MPa
|
14.3 14.3
|
|
Tensile Strength, psi拉伸強度，psi
|
2075 2075
|
|
Tg, °C TG°C
|
-32 -32
|
|
Low Temperature Brittle Point, °C低溫脆化點℃
|
-44 -44
|
|
Low Temp Gehman T10,000 PSI, °C低溫格曼T10，000 PSI，°C
|
-36 -36
|
|
Volatilization揮發
|
-13 -13
|
|
Immersion/Extraction, Weight change, %浸入/提取，重量變化，％
|
|
|
Hexane正己烷
|
-24 -24
|
|
1% Soap Solution 1％的肥皂溶液
|
-8.4 -8.4
|
|
Cottonseed Oil棉籽油
|
-17 -17
|
|
Distilled water蒸餾水
|
-1.4 -1.4
|
|
High humidity高濕度
|
-1.0 -1.0
|
|
ABS ABS
|
Good好
|
|
Polystyrene聚乙烯
|
Poor差
|
|
|
|
點擊圖片查看大圖