TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 50 mm/min
|
560
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
510
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
6
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
98
|
%
|
ASTM D 638
|
|
Tensile Modulus, 50 mm/min
|
20500
|
kgf/cm2
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
940
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
22700
|
kgf/cm2
|
ASTM D 790
|
|
Hardness, Rockwell L
|
89
|
-
|
ASTM D 785
|
|
Hardness, Rockwell R
|
121
|
-
|
ASTM D 785
|
|
Tensile Stress, yield, 50 mm/min
|
57
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min
|
60
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
6
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min
|
120
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
2150
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
85
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
2250
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, notched, 23°C
|
88
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
78
|
cm-kgf/cm
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C
|
714
|
cm-kgf
|
ASTM D 3763
|
|
Izod Impact, unnotched 80*10*3 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched 80*10*3 -30°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*3 +23°C
|
70
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*3 -30°C
|
60
|
kJ/m2
|
ISO 180/1A
|
|
Charpy 23°C , V-notch Edgew 80*10*3 sp=62mm
|
70
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy -30°C , V-notch Edgew 80*10*3 sp=62mm
|
65
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy 23°C , Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
Charpy -30°C , Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50
|
145
|
°C
|
ASTM D 1525
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
139
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
124
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C , flow
|
6.96E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C , xflow
|
7.47E-05
|
1/°C
|
ASTM E 831
|
|
CTE, 23°C to 80°C , flow
|
7.2E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 80°C , xflow
|
7.2E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
Passes
|
-
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate B/50
|
145
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
146
|
°C
|
ISO 306
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
140
|
°C
|
ISO 75/Be
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
128
|
°C
|
ISO 75/Ae
|
|
Relative Temp Index, Elec
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact
|
120
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact
|
125
|
°C
|
UL 746B
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.18
|
-
|
ASTM D 792
|
|
Mold Shrinkage, flow, 3.2 mm
|
0.4 - 0.8
|
%
|
SABIC Method
|
|
Mold Shrinkage, xflow, 3.2 mm
|
0.4 - 0.8
|
%
|
SABIC Method
|
|
Melt Flow Rate, 300°C /1.2 kgf
|
10
|
g/10 min
|
ASTM D 1238
|
|
Density
|
1.19
|
g/cm2
|
ISO 1183
|
|
Water Absorption, (23°C /sat)
|
0.35
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.15
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 300°C /1.2 kg
|
9
|
cm3/10 min
|
ISO 1133
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
Volume Resistivity
|
>1.E+15
|
Ohm-cm
|
ASTM D 257
|
|
Surface Resistivity
|
>1.E+15
|
Ohm
|
ASTM D 257
|
|
Dielectric Strength, in oil, 0.8 mm
|
16.2
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity, 100 Hz
|
2.68
|
-
|
ASTM D 150
|
|
Relative Permittivity, 1 MHz
|
2.64
|
-
|
ASTM D 150
|
|
Dissipation Factor, 100 Hz
|
0.0012
|
-
|
ASTM D 150
|
|
Dissipation Factor, 1 MHz
|
0.0093
|
-
|
ASTM D 150
|
|
FLAME CHARACTERISTICS
|
Value
|
Unit
|
Standard
|
|
UL Recognized, 94HB Flame Class Rating (3)
|
0.4
|
mm
|
UL 94
|
|
Glow Wire Flammability Index 850°C , passes at
|
0.8
|
mm
|
IEC 60695-2-12
|
|
Glow Wire Flammability Index 960°C , passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
Glow Wire Ignitability Temperature, 1.0 mm
|
875
|
°C
|
IEC 60695-2-13
|
|
Glow Wire Ignitability Temperature, 3.0 mm
|
875
|
°C
|
IEC 60695-2-13
|
點擊圖片查看大圖